Enamel reaction tank

How to prevent enamel peeling off in enamel reaction tank? This is the problem we need to solve in this issue. The answer to this question is explained below. Please refer to the summary below.
1. Avoid vibration and external impact during transportation of enamel reaction tank.
2. Do not add particles when using the reaction kettle, and even if added, do not stir to avoid damaging the enamel surface. If there are minor issues such as enamel peeling, cracks, etc., JS916 should be used immediately for repair.

3. Prevent solvent corrosion of enamel reaction vessel metal body, causing unnecessary shutdown and equipment scrapping.

4. In the use of the reaction vessel, if the maintenance is improper and a large area falls off, it is recommended to return to the factory for re glazing.
4. The reaction kettle is formed by spraying high silicon content porcelain glaze on the surface of low-carbon steel tires and baking it at a high temperature of around 900 degrees Celsius to tightly adhere the porcelain glaze to the surface of the metal steel tire.
5. Due to the different mechanical and physical properties of these two materials, the reasons for damage to enamel reaction tank are also diverse. There are generally several reasons for mechanical damage, working temperature effects, processing stress damage, electrostatic breakdown, hydrogen evolution corrosion, and substrate failure.
The above is the main content of this enamel reaction tank. The working temperature of the reaction vessel has a significant impact on the use of the enamel glass reaction vessel. If the stress generated by the enamel exceeds its service stress due to large temperature changes, the enamel will be damaged.